性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
基本性能 | 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 20 | g/10min |
密度 | ASTM D-792 | 0.954 | g/cm3 | ||
机械性能 | 硬度 | ASTM D-2240 | 57 | Shore D | |
屈服伸长率 | ASTM D-638 | 7 | % | ||
耐环境应力开裂性 | 122℉(50℃),F50,100%lgepal,hrs | ASTM D-1693 | 3 | ||
2%割线弯曲模量 | ASTM D-790 B | 167,000(1151) | psi(MPa) | ||
拉伸冲击强度 | ASTM D-1822,Type S | 20(42) | ft·lb/in2(kJ/m2) | ||
断裂拉伸强度 | ASTM D-638 | 2000(14) | psi(MPa) | ||
断裂伸长率 | ASTM D-638 | 250 | % | ||
屈服拉伸强度 | ASTM D-638 | 4100(28) | psi(MPa) | ||
热性能 | 维卡软化点 | ASTM D-1525 | 261(127) | ℉(℃) | |
DSC结晶点 | Dow Method | 243(117) | ℉(℃) | ||
热变形温度 | 66psi(0.45MPa) | ASTM D-648 | 163(73) | ℉(℃) | |
脆化温度 | ASTM D-746 | <-105(<-76) | ℉(℃) | ||
DSC熔点 | Dow Method | 266(130) | ℉(℃) |