| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 熔体流动速率 | 条件G | ASTM D-1238 | 5.0 | g/10min |
| 熔体流动速率 | 条件I | ASTM D-1238 | 25.0 | g/10min | |
| 比重 | ASTM D-792 | 1.06 | 23/23℃ | ||
| 机械性能 | 洛氏硬度 | ASTM D-785 | 83 | M | |
| 弯曲强度 | ASTM D-790 | 960(13600) | kg/cm2(lb/in2) | ||
| IZOD冲击强度 | 1/8〃 | ASTM D-256 | 1.8(0.33) | kg.cm/cm(ft.ld/in) | |
| 弯曲弹性率 | ASTM D-790 | 3.4(4.9) | 10kg/cm2(10lb/in2) | ||
| 引张强度 | ASTM D-638 | 700(9920) | kg/cm2(lb/in2) | ||
| IZOD冲击强度 | 1/4〃 | ASTM D-256 | 1.7(0.31) | kg.cm/cm(ft.ld/in) | |
| 伸长率 | ASTM D-638 | 3.0 | % | ||
| 热性能 | 维卡软化点 | ASTM D-1525 | 104(219) | ℃(℉) | |
| 热变形温度 | ASTM D-785 | 90(194) | ℉ | ||
| 热变形温度 | ASTM D-785 | 100(212) | ℃ | ||
| 燃烧率 | 1/16"HB | ||||